M. R. Zamanzad-Ghavidel,, K. Raeissi, A. Saatchi. EFFECT OF SUBSTRATE TEXTURE AND DEPOSITION CURRENT DENSITY ON PROPERTIES OF NiNANOCRYSTALLINE ELECTRODEPOSITS. IJMSE 2012; 9 (2) :1-14
URL: http://ijmse.iust.ac.ir/article-1-435-en.html
Abstract:   (26726 Views)
Abstract: Nickel was electrodeposited onto copper substrates with high {111} and {400} peak intensities. The grain size of coatings deposited onto the copper substrate with a higher {111} peak intensity was finer. Spheroidized pyramid morphology was obtained at low current densities on both copper substrates. By increasing the deposition current density, grain size of the coating was increased for both substrates and eventually a mixed morphology of pyramids and blocks was appeared without further increase in grain size. This decreased the anodic exchange current density probably due to the decrease of surface roughness and led to a lower corrosion rate.
Full-Text [PDF 2425 kb]   (6295 Downloads)    
Type of Study: Research Paper |

Add your comments about this article : Your username or Email:
CAPTCHA

Send email to the article author


Rights and permissions
Creative Commons License This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.

© 2022 All Rights Reserved | Iranian Journal of Materials Science and Engineering

Designed & Developed by : Yektaweb